Eurasia Petrol is an independent petroleum trading company based in Antalya, Turkey. It is ideally located in the region’s business hub and in the middle of the world’s largest energy producing region.
- Product Category
- POPOLYMER
- Product Name
- POLYETHYLENE – HDPE
- Grade
- 52518
| PROPETY | Unit | Value | Test Method |
|---|---|---|---|
| Density | (g/ml) | 0.952 | ASTM D 1505 |
| MFR(190°C/2.16kg) | (g/10min) | 18 | ASTM D 1238 |
| Flexural modulus | (MPa) | 1350 | ASTM D 790 |
| Notched Izod impact at 23°C | (J/m) | 25 | ASTM D 256/A |
| Vicat softening point | (°C) | 122 | ASTM D 1525 |
PRODUCT DATA SHEET
POLYETHYLENE | HDPE | BL3
- Product Category
- POLYMER
- Product Name
- POLYETHYLENE – HDPE
- Grade
- BL3
| PROPETY | Test Method | Unit | Value |
|---|---|---|---|
| Mass density (230C) | ISO 1183 | g/cm3 | 0.954 |
| Melt Flow Rate (1900C/5.0kg) | ISO 1133 | g/10min | 1.2 |
| Melt Flow Rate (1900C/21.6 kg) | ISO 1133 | g/10min | 23 |
| Stress at Yield | ISO 527 | MPa | 26 |
| Flexural Creep Modulus (4point,1min) | DIN 19537-2 | MPa | 1300 |
| Tensile Modulus (230C, v = 1mm / min ,Secant) | ISO 527 | MPa | 1250 |
| Stress at Break | ISO 527 | MPa | 32 |
| Elongation at Break | ISO 527 | % | >600 |
| Elongation at yield | ISO 527 | % | 10 |
| Softening Temperature | ISO 306 | 0C | 77 |
| Brittle Temperature | ASTM D746-72 | 0C | < - 80 |
| Shore D hardness | ISO 868 | - | 62 |
| ESCR in Full Notch Creep Test (800C, 2% Arcopal h@3.5 MPa | ISO CD 16770 | ||
| Impact strength (230C) | ISO 179/1eA | Kj/m2 | 10 |
| Swell ratio | Internal | % | 120 |
PRODUCT DATA SHEET
POLYETHYLENE | HDPE | EX3
- Product Category
- POLYMER
- Product Name
- POLYETHYLENE – HDPE
- Grade
- EX3
| PROPETY | Unit | Typical Value | Test Method |
|---|---|---|---|
| Mass density (230 C) | g/cm3 | 0.956 | ISO 1183 |
| Melt Flow Rate (1900C/5.0kg) | g/10min | 3.3 | ISO 1183 |
| Melt Flow Rate (1900C/21.6kg) | g/10min | 33 | ISO 1183 |
| Stress at Yield | MPa | 27 | ISO 527 |
| Flexural Creep Modulus (4point, 1min) | MPa | 1350 | DIN 19537-2 |
| Tensile Modulus (230 C, v = 1mm / min ,Secant) | MPa | 1200 | ISO 527 |
| Stress at Break | MPa | 31 | ISO 527 |
| Elongation at Break | % | >1000 | ISO 527 |
| Elongation at yield | % | 10 | ISO 527 |
| Softening Temperature | 0C | 8 | ISO 306 |
| Brittle Temperature | 0C | < - 80 | ASTM D746-72 |
| Shore D hardness | - | 62 | ISO 868 |
| ESCR in Full Notch Creep Test (800C, 2% Arcopal ) | h@2.5 MPa | 2 | ISO CD 16770 |
| Impact strength (230C) | Kj/m2 | 23 | ISO 179/1eA |
PRODUCT DATA SHEET
POLYETHYLENE | HDPE | EX5
- Product Category
- POLYMER
- Product Name
- POLYETHYLENE – HDPE
- Grade
- EX5
| PROPETY | Test Method | Unit | Value |
|---|---|---|---|
| Mass density (230 C) | ISO 1183 | g/cm3 | 0.949 |
| Melt Flow Rate (1900C/5.0kg) | ISO 1133 | g/10min | 0.28 |
| Melt Flow Rate (1900C/21.6kg) | ISO 1133 | g/10min | 8 |
| Stress at Yield | ISO 527 | MPa | 24 |
| Stress at Break | ISO 527 | MPa | 35 |
| Softening Temperature | ISO 306 | 0C | 75 |
| Brittle Temperature | ASTM D746-72 | 0C | < - 80 |
| Shore D hardness | ISO 868 | - | 60 |
| Max. tensile strength MD / TD | ISO 527 | MPa | 45/40 |
| Tear strength MD / TD | ISO 6383-2 | m N | 200/450 |
| Max. elongation MD / TD | ISO 527 | % | 400/450 |
| Dart Drop Impact | ASTM D 1709 | g | 220 |
PRODUCT DATA SHEET
POLYETHYLENE | HDPE | HB – 0035
- Product Category
- POLYMER
- Product Name
- POLYETHYLENE – HDPE
- Grade
- HB – 0035
| PROPETY | Test Method | Unit | Value |
|---|---|---|---|
| Mass density (230 C) | ASTM D 1505 | g/cm3 | 0.959 |
| Melt Flow Rate (1900 C/2.16 kg) | ASTM D1238 | g/10min | 0.35 |
| Izod impact strength | ASTM D 256 | Kg.cm/cm | 25 min |
| Yellow index | ASTM D 1925 | - | -5 max |
| Ash content | ASTM D 1063 | wt% | 0.06 max |
| Volatile matter | ASTM D 1960 | wt% | 0.05 max |
| Tensile strength @ break | ASTM D 638 | gr/cm2 | 290 min |
| Elongation @ break | ASTM D 638 | % | 900 min |
| Melting point | ASTM D 2117 | oC | 130 |
| Vicat softening point | ASTM D 1525 | oC | 126 |
| ESCR | ASTM D 1693 | hr | 15 |
PRODUCT DATA SHEET
POLYETHYLENE | HDPE | PE – 80
- Product Category
- POLYMER
- Product Name
- POLYETHYLENE – HDPE
- Grade
- EX3-80_HM5010T2N – PE 80
| PROPETY | Test Method | Unit | Value |
|---|---|---|---|
| Mass density (230C) | ISO 1183 | g/cm3 | 0.945 |
| Melt Flow Rate (1900C/5.0kg) | ISO 1133 | g/10min | 0.45 |
| Melt Flow Rate (1900 C/21.6 kg) | ISO 1133 | g/10min | 12 |
| Stress at Yield | ISO 527 | MPa | 22 |
| Flexural Creep Modulus (4point, 1min) | DIN 19537-2 | MPa | 950 |
| Tensile Modulus (230C, v = 1mm / min ,Secant) | ISO 527 | MPa | 850 |
| Stress at Break | ISO 527 | MPa | 35 |
| Elongation at Break | ISO 527 | % | >850 |
| Elongation at yield | ISO 527 | % | 8 |
| Softening Temperature | ISO 306 | 0 C | 67 |
| Brittle Temperature | ASTM D746-72 | 0 C | < - 80 |
| Shore D hardness | ISO 868 | - | 60 |
| ESCR in Full Notch Creep Test (800 C, 2% Arcopal ) | ISO CD 16770 | h@4.0 MPa | 50 |
| Impact strength (230 C) | ISO 179/1eA | Kj/m2 | 23 |
| Expected Properties on Application | |||
| S4 Test (RCP) | ISO DIS 13477 | Bar | Pc> 3 |
| Notch Test (SCG) | ISO DIS 13479 | h@4.0 MPa | >250 |
| Hydrostatic strength test (800 C) | ISO 1167 | h@4.6 MPa | >1000 |
PRODUCT DATA SHEET
POLYETHYLENE | HDPE | PE – 100
- Product Category
- POLYMER
- Product Name
- POLYETHYLENE – HDPE
- Grade
- EX3100S_HMCRP100 N PE 100
| PROPETY | Test Method | Unit | Value |
|---|---|---|---|
| Mass density (230C) | ISO 1183 | g/cm3 | 0.94 |
| Melt Flow Rate (1900C/5.0kg) | ISO 1133 | g/10min | 0.22 |
| Melt Flow Rate (1900C/21.6 kg) | ISO 1133 | g/10min | 6.2 |
| stress at Yield | ISO 527 | MPa | 23 |
| Flexural Creep Modulus (4point, 1min) | DIN 19537-2 | MPa | 1050 |
| Tensile Modulus (230C, v = 1mm / min ,Secant) | ISO 527 | MPa | 850 |
| Stress at Break | ISO 527 | MPa | 36 |
| Elongation at Break | ISO 527 | % | >1000 |
| Elongation at yield | ISO 527 | % | 10 |
| Softening Temperature | ISO 306 | 0C | 74 |
| Brittle Temperature | ASTM D746-72 | 0C | < - 80 |
| Shore D hardness | ISO 868 | 62 | |
| ESCR in Full Notch Creep Test (800C, 2% rcopal ) | ISO CD 16770 | h@4.0 MPa | 400 |
| Impact strength (230C) | ISO 179/1eA | Kj/m2 | 25 |
| S4 Test (RCP) | ISO DIS 13477 | Bar | Pc> 20 |
| Notch Test (SCG) | ISO DIS 13479 | h@4.6 MPa | >1000 |
| Hydrostatic strength test (800c) | ISO 1167 | h@4.6 MPa | >15000 |