Eurasia Petrol is an independent petroleum trading company based in Antalya, Turkey. It is ideally located in the region’s business hub and in the middle of the world’s largest energy producing region.
- Product Category
- POPOLYMER
- Product Name
- POLYETHYLENE – LLDPE
- Grade
- LL 0209 AA
| PROPERTY | Test Method | Unit | Value |
|---|---|---|---|
| MFI@190° C, 2.16 kg | D1238 | gr/10min | 0.9 |
| Density | D2839 | gr/ml | 0.92 |
| Vicat Softening Point | D1525 | °C | 100 |
| Tensile Strength @Yield, MD/TD | D638 | Mpa | 10.5/11 |
| Elongation @ Break, MD/TD | D638 | % | 620/840 |
| Tensile Strength @ Break, MD/TD | D688 | Mpa | 41/32 |
| Tear Strength, MD/TD | D1922 | gr/25mic | 145/370 |
| Impact Strength, Dart | D1709 | gr | 150 |
| Haze | D1003 | % | 10 |
| Gloss (45°) | D2457 | Rating | 56 |
PRODUCT DATA SHEET
POLYETHYLENE | LLDPE | LL0209 KJ
- Product Category
- POPOLYMER
- Product Name
- POLYETHYLENE – LLDPE
- Grade
- LL0209 KJ
| PROPERTY | Test Method | Unit | Value |
|---|---|---|---|
| MFI@190° C, 2.16 kg | D1238 | gr/10min | 0.9 |
| Density | D2839 | gr/ml | 0.92 |
| Vicat Softening Point | D1525 | °C | 100 |
| Tensile Strength @ Yield, MD/TD | D638 | Mpa | 10.5/11 |
| Elongation @ Break, MD/TD | D638 | % | 620/840 |
| Tensile Strength @ Break, MD/TD | D688 | Mpa | 41/32 |
| Tear Strength, MD/TD | D1922 | gr/25mic | 145/370 |
| Impact Strength, Dart | D1709 | gr | 150 |
| Haze | D1003 | % | 10 |
| Gloss (45°) | D2457 | Rating | 56 |
PRODUCT DATA SHEET
POLYETHYLENE | LLDPE | LL0220 AA
- Product Category
- POPOLYMER
- Product Name
- POLYETHYLENE – LLDPE
- Grade
- LL0220 AA
| PROPERTY | Test Method (ASTM) | Unit | Value |
|---|---|---|---|
| Density | 0.92 | g/cm3 | ISO1183 |
| Melt Flow Rate (190°C /2.16kg) | 2.2 | g/10min | ISO1133 |
| Melting point | °C | ISO3146 | |
| Vicat softening temperature, A/50 | 93 | °C | ISO306 |
| Impact Strength | Gr | 130 | ASTM D1709 |
| Tear Strength TD | G/25μ | 300 | ASTM D1922 |
| Tear Strength MD | G/25μ | 110 | ASTM D1922 |
| Yield Stress TD | MPa | 11 | ISO 527 |
| Yield Stress MD | MPa | 10 | ISO 527 |
| Tensile Strength TD | MPa | 28 | ISO 527 |
| Tensile Strength MD | MPa | 36 | ISO 527 |
| Elongation at break TD | % | 800 | ISO 527 |
| Elongation at break MD | % | 600 | ISO 527 |
| Modulus of elasticity TD | MPa | ISO 527 |
PRODUCT DATA SHEET
POLYETHYLENE | LLDPE | LL 0220 KJ
- Product Category
- POLYMER
- Product Name
- POLYETHYLENE – HDPELPOLY
- Grade
- EX5
| PROPERTY | Test Method | Unit | Value |
|---|---|---|---|
| MFI(190°C /2.16Kg) | ASTM D 1238 | ASTM D 1238 | 2.3 |
| MFI(190°C /21.6Kg) | ASTM D 1238 | ASTM D 1238 | - |
| Density | ASTM D 1505 | Gr/cm³ | 0.92 |
| Haze | ASTM D 1003 | % | 12 |
| Gloss(45°) | ASTM D 2457 | % | 30 |
| Anti-Oxidant | √ | ||
| Anti-Block | √ | ||
| Slip Agent | √ | ||
| Dart Drop Impact | ASTM D1709(A) | G | 90 |
| Tear Strength MD/TD | ASTM D 1922 | Gr/25μm | 100/300 |
| Tensile Strength at yield MD/TD | ASTM D 882 | MPa | 43019 |
| Tensile Strength at Break MD/TD | ASTM D 882 | MPa | 30/25 |
| Elongation at Break MD/TD | ASTM D 882 | % | 1000/1100 |
| Secant Modulus MD/TD | ASTM D 882 | MPa | 80/100 |
| Coefficient of friction | ASTM D1894 | - | 0.13 |
| Vicat Softening Temperature | ASTM D 1525 | °C | 100 |
| Melting Point | BPC | °C | 123 |
PRODUCT DATA SHEET
POLYETHYLENE | LLDPE | 22501
- Product Category
- POPOLYMER
- Product Name
- POLYETHYLENE – LLDPE
- Grade
- 22501
| PROPERTY | Test Method | Unit | Value |
|---|---|---|---|
| density | ASTM D 1505 | (g/ml) | 0.922 |
| MFR(190°C/2.16kg) | ASTM D 1238 | (g/10min) | 0.95 |
| Dart Impact | ASTM D 1709 | (g) | 80 |
| Elmendorf Tear MD/TD | ASTM D 1922 | (g) | 105/460 |
| Tensile strength at yield MD/TD | ASTM D 882 | (MPa) | 13/12.5 |
| Tensile strength at Break MD/TD | ASTM D 882 | (MPa) | 45/30 |
| Ultimate Elongation MD/TD | ASTM D 882 | (%) | 680/780 |
| 2% Secant modulus MD/TD | ASTM D 882 | (MPa) | 200/240 |
| Haze | ASTM D 1003 | (%) | 21 |
| Gloss 45° | ASTM D 245 | (%) | 38 |