Eurasia Petrol is an independent petroleum trading company based in Antalya, Turkey. It is ideally located in the region’s business hub and in the middle of the world’s largest energy producing region.
- Product Category
- POPOLYMER
- Product Name
- POLYETHYLENE – LDPE
- Grade
- 2102047 – 37
| PROPERTY | Value | Unit | Test Method |
|---|---|---|---|
| Physical Properties | ISO1133 | ||
| MFI (190 0C /2 .16 Kg ) | 4.7 | dg/min | ISO 1183 (A) |
| Density | 920 | Kg/m3 | |
| Impact strength | 15 | KJ/m | ASTM D 4272 |
| Tear strength (TD) | 25 | KN/m | ISO 6383-2 |
| Tear Strength (MD) | 80 | KN/m | ISO 6383-2 |
| Yield stress (TD) | 11 | MPa | ISO 527 |
| Yield stress (MD) | 12 | MPa | ISO 527 |
| Tensile Stress at break (TD) | 15 | MPa | ISO 527 |
| Tensile Stress at break (MD) | 27 | MPa | ISO 527 |
| Strain at Break (TD) | >500 | % | ISO 527 |
| Strain at Break (MD) | 100 | % | ISO 527 |
| Modulus of Elasticity (TD) | 200 | MPa | ISO 527 |
| Modulus of Elasticity (MD) | 200 | MPa | ISO 527 |
| Coefficient of friction | 0.2 | ASTM D 1894 | |
| Blocking | 20 | g | SABTEC method |
| Re-blocking | 10 | g | SABTEC method |
| Haze | 9 | % | ASTM D 1003A |
| Gloss(45o) | 55 | % | ASTM D 2457 |
| Clarity | 21 | mV |
PRODUCT DATA SHEET
POLYETHYLENE | LDPE | 2100TN00
- Product Category
- POPOLYMER
- Product Name
- POLYETHYLENE – LDPE
- Grade
- 2100TN00
| PROPERTY | Test Method | Unit | Value |
|---|---|---|---|
| MFI (200 o c/5kg ) | ISO 1133 | g/10 min | 0.3 |
| Density | ISO 1183 (A) | Kg/m3 | 921 |
| Haze | ASTM D 1003 (A) | % | 15 |
| Clarity | DSM Method | mV | 56 |
| Gloss | ASTM D2457 | % | 39±5 |
| Anti Oxidant | DSM Method | ppm | 600±60 |
| Anti Block | - | ppm | - |
| Slip | - | ppm | - |
| Impact Strength | ASTM D4272 | kJ/m | 35 |
| Tear strength TD | ISO 6383-2 | KN/m | 25 |
| Tear strength MD | ISO 6383-2 | KN/m | 20 |
| Yield Stress TD | ISO R527-1 | MPa | 11 |
| Yield Stress MD | ISO R527-1 | MPa | 12 |
| Tensile strength TD | ISO R527-1 | MPa | 26 |
| Tensile strength MD | ISO R527-1 | MPa | 29 |
| Elongation @ break TD | ISO R527-1 | % | >500 |
| Elongation @ break MD | ISO R527-1 | % | >200 |
| Modulus of elasticity TD | ISO R527-1 | MPa | 190 |
| Modulus of elasticity MD | ISO R527-1 | MPa | 180 |
| Co efficient of friction | ASTM D1894 | - | 0.7 |
PRODUCT DATA SHEET
POLYETHYLENE | LDPE | 2102TX00
- Product Category
- POLYMER
- Product Name
- POLYETHYLENE – LDPE
- Grade
- 2102TX00
| PROPERTY | Test Method | Unit | Value |
|---|---|---|---|
| MFI | ISO 1133 | g/10 min | 1.9 |
| Density | ISO 1183 (A) | Kg/m3 | 921 |
| Haze | ASTM D 1003 (A) | % | 11 |
| Clarity | DSM Method | mV | 29 |
| Gloss | ASTM D2457 | % | 50±5 |
| Anti Oxidant | DSM Method | ppm | 600±60 |
| Anti Block | - | ppm | - |
| Slip | - | ppm | - |
| Impact Strength | ASTM D4272 | kJ/m | 26 |
| Tear strength TD | ISO 6383-2 | KN/m | 25 |
| Tear strength MD | ISO 6383-2 | KN/m | 60 |
| Yield Stress TD | ISO R527-1 | MPa | 11 |
| Yield Stress MD | ISO R527-1 | MPa | 13 |
| Tensile strength TD | ISO R527-1 | MPa | 20 |
| Tensile strength MD | ISO R527-1 | MPa | - |
| Elongation @ break TD | ISO R527-1 | % | >500 |
| Elongation @ break MD | ISO R527-1 | % | >150 |
| Modulus of elasticity TD | ISO R527-1 | MPa | 200 |
| Modulus of elasticity MD | ISO R527-1 | MPa | 190 |
| Co efficient of friction | ASTM D1894 | - | >1.0 |
PRODUCT DATA SHEET
POLYETHYLENE | LDPE | 2119
- Product Category
- POLYMER
- Product Name
- POLYETHYLENE – LDPE
- Grade
- 2119
| PROPERTY | Value | Unit | Test Method |
|---|---|---|---|
| MFI(190 0C /2 .16 Kg ) | 1.9 | dg/min | ISO1133 |
| Density | 921 | Kg/m3 | ISO 1183 (A) |
| Impact strength | 26 | KJ/m | ASTM D 4272 |
| Tear strength (TD) | 25 | KN/m | ISO 6383-2 |
| Tear Strength (MD) | 60 | KN/m | ISO 6383-2 |
| Yield stress (TD) | 11 | MPa | ISO 527 |
| Yield stress (MD) | 13 | MPa | ISO 527 |
| Tensile stress at break (TD) | 20 | MPa | ISO 527 |
| Tensile stress at break (MD) | 35 | MPa | ISO 527 |
| Strain at Break (TD) | >500 | % | ISO 527 |
| Strain at Break (MD) | >150 | % | ISO 527 |
| Modulus of Elasticity (TD) | 200 | MPa | ISO 527 |
| Modulus of Elasticity (MD) | 190 | MPa | ISO 527 |
| Coefficient of friction | >1 | ASTM D 1894 | |
| Blocking | 20 | g | SABTEC method |
| Re-blocking | 100 | g | SABTEC method |
| Haze | 9 | % | ASTM D 1003A |
| Gloss (45o) | 55 | % | ASTM D 2457 |
| Clarity | 26 | mV |
PRODUCT DATA SHEET
POLYETHYLENE | LDPE | 2420 H
- Product Category
- POPOLYMER
- Product Name
- POLYETHYLENE – LDPE
- Grade
- 2420 H
| PROPERTY | Value | Unit | Test Method |
|---|---|---|---|
| Mass Density (23 °C) | 0.924 | g/cm3 | ISO1183 |
| Melt Flow Rate (190°C /2.16kg) | 2 | g/10min | ISO1133 |
| Melting point | 112 | °C | ISO11357 |
| Vicat softening temperature, A/50 | 95 | °C | ISO306 |
| Tensile Modulus of Elasticity | 270 | MPa | ISO527 |
| Stress at Yield | 11 | MPa | ISO527 |
| Shore D hardness | 48 | － | ISO868 |
| Max. tensile strength MD | 23 | MPa | ISO527 |
| Max. tensile strength TD | 21 | MPa | ISO527 |
| Maximum elongation MD | 580 | % | ISO527 |
| Maximum elongation TD | 700 | % | ISO527 |
| Dart Drop Impact | 110 | g | ASTM D1709 |
| Gloss ( 60°) | 120 | － | ASTM D2457 |
| Haze (40μm film) | 6.5 | % | ASTM D1003 |
PRODUCT DATA SHEET
POLYETHYLENE | HDPE | 2420D
- Product Category
- POPOLYMER
- Product Name
- POLYETHYLENE – LDPE
- Grade
- 2420D
| PROPERTY | Value | Unit | Test Method |
|---|---|---|---|
| MFI(190 0C /2 .16 Kg ) | 0.25 | g/cm3 | ISO1133 |
| Mass Density (23 DC) | 0.923 | Kg/m3 | ISO 1183 |
| Melting point | 113 | °C | ISO11357 |
| Vicat softening temperature, A/50 | 95 | °C | ISO306 |
| Tensile Modulus of Elasticity | 260 | MPa | ISO527 |
| Stress at Yield | 10 | MPa | ISO527 |
| Shore D hardness | 48 | ISO868 | |
| Max. tensile strength MD | 25 | MPa | ISO527 |
| Max. tensile strength TD | 24 | MPa | ISO527 |
| Maximum elongation MD | 600 | % | ISO527 |
| Maximum elongation TD | 650 | % | ISO527 |
| Dart Drop Impact | 270 | g | ASTM D1709 |
| Gloss ( 60°) | 100 | － | ASTM D2457 |
| Haze (40μm film) | 8.5 | % | ASTM D1003 |
PRODUCT DATA SHEET
POLYETHYLENE | LDPE | LH0075
- Product Category
- POPOLYMER
- Product Name
- POLYETHYLENE – LDPE
- Grade
- LH0075
| PROPERTY | Test Method | Unit | Value |
|---|---|---|---|
| MFI (190 C/2. 16 kg) | ASTM D 1238 | gr/10 min | 0.75 |
| Density | TSTM 209 B | gr/ml | 0.921 |
| Vicat softening point | ASTM D 1525 | C | 94 |
| Elongation @ break (MD) | ASTM D882 | % | 300 min. |
| Elongation @ break (TD) | ASTM D 882 | % | 450 min. |
| Tensile @ break (MD) | ASTM D 882 | kg/cm2 | 170 min |
| HDT | ASTM D 648 | oC | 33 |
| Dart impact | ASTM D 1709 | gr | 120 min |