PROPERTY | Value | Unit | Method |
Melt Flow Rate (230 oC, 2.16kg) | 3 | g/10min | ASTM D1238 |
Density | 0.9 | g/cm3 | ASTM D1505 |
Flexural Modulus | 1550 | MPa | ASTM D790 |
Tensile Strength at Yield | 35 | MPa | ASTM D638 |
Tensile Elongation at Yield | 12 | % | ASTM D638 |
Izod Impact Strength (notched) at 23 oC | 55 | J/m | ASTM D256 |
Vicat softening point (10N) | 156 | oC | ASTM D1525 |
H.D.T. (0.46 Mpa) | 94 | oC | ASTM D648 |
用途
- 030 用于高品质热成型的硬板,例如自动售货杯,乳制品包装和水果托盘,饼干和巧克力的托盘。薄膜纱线、酒椰纤维、胶带、捆扎带。地毯背衬、袋子、工业面料、地垫和人造草。打包机麻线,包装麻绳和绳索刷子,扫帚和各种用途的PP网
PROPERTY | Value | Unit | Method |
Melt Flow Rate (230 oC, 2.16kg) | 6 | g/10min | ASTM D1238 |
Density | 0.9 | g/cm3 | ASTM D1505 |
Flexural Modulus | 1550 | MPa | ASTM D790 |
Tensile Strength at Yield | 35 | MPa | ASTM D638 |
Tensile Elongation at Yield | 12 | % | ASTM D638 |
Izod Impact Strength (notched) at 23 oC | 30 | J/m | ASTM D256 |
Vicat softening point (10N) | 154 | oC | ASTM D1525 |
H.D.T. (0.46 Mpa) | 94 | oC | ASTM D648 |
用途
- 在薄膜纱线行业生产袋子和重型巨型袋大包和打包机麻线、包装麻绳和绳索刷子,文具文件夹薄板. 热成型片材. 汽车工业、玩具和花园家具的零件
PROPERTY | Value | Unit | Method |
Melt Flow Rate (230 oC, 2.16kg) | 6 | g/10min | ASTM D1238 |
Density | 0.9 | g/cm3 | ASTM D1505 |
Flexural Modulus | 1400 | MPa | ASTM D790 |
Tensile Strength at Yield | 26 | MPa | ASTM D638 |
Tensile Elongation at Yield | 9 | % | ASTM D638 |
Izod Impact Strength (notched) at 23 oC | 170 | J/m | ASTM D256 |
Vicat softening point (10N) | 152 | oC | ASTM D1525 |
H.D.T. (0.46 Mpa) | 95 | oC | ASTM D648 |
用途
- 包装、汽车和消费品行业、行李、油漆桶、水桶、容器、板条箱、电池和大型玩具。
PROPERTY | Value | Unit | Method |
Melt Flow Rate (230 oC, 2.16kg) | 25 | g/10min | ASTM D1238 |
Rockwell Hardness | 100 | R.Scale | ASTM D785 |
Flexural Modulus | 1500 | MPa | ASTM D790 |
Tensile Strength at Yield | 32 | MPa | ASTM D638 |
Tensile Elongation at Yield | 13 | % | ASTM D638 |
Izod Impact Strength (notched) at 23 oC | 30 | J/m | ASTM D256 |
Vicat softening point (10N) | 152 | oC | ASTM D1525 |
H.D.T. (0.46 Mpa) | 94 | oC | ASTM D648 |
用途
- 高熔体流动均聚物聚丙烯,用于以中高速纺丝生产 CF、BCF 和短纤维。适用于无纺布、尿布、医疗卫生应用和湿巾的低旦短纤维。