| PROPERTY | Value | Unit | Method |
| Melt Flow Rate (230 oC, 2.16kg) | 3 | g/10min | ASTM D1238 |
| Density | 0.9 | g/cm3 | ASTM D1505 |
| Flexural Modulus | 1550 | MPa | ASTM D790 |
| Tensile Strength at Yield | 35 | MPa | ASTM D638 |
| Tensile Elongation at Yield | 12 | % | ASTM D638 |
| Izod Impact Strength (notched) at 23 oC | 55 | J/m | ASTM D256 |
| Vicat softening point (10N) | 156 | oC | ASTM D1525 |
| H.D.T. (0.46 Mpa) | 94 | oC | ASTM D648 |
用途
- 030 硬质片材，用于高质量的热成型，例如自动售货杯、乳制品包装以及水果、饼干和巧克力的托盘。 薄膜纱线、拉菲草、胶带、捆扎带。 地毯背衬、袋子、工业织物、垫子和人造草坪。 .
| PROPERTY | Value | Unit | Method |
| Melt Flow Rate (230 oC, 2.16kg) | 6 | g/10min | ASTM D1238 |
| Density | 0.9 | g/cm3 | ASTM D1505 |
| Flexural Modulus | 1550 | MPa | ASTM D790 |
| Tensile Strength at Yield | 35 | MPa | ASTM D638 |
| Tensile Elongation at Yield | 12 | % | ASTM D638 |
| Izod Impact Strength (notched) at 23 oC | 30 | J/m | ASTM D256 |
| Vicat softening point (10N) | 154 | oC | ASTM D1525 |
| H.D.T. (0.46 Mpa) | 94 | oC | ASTM D648 |
用途
- 在薄膜纱线行业生产袋子和重型巨型袋大包和打包机麻线、包装麻绳和绳索刷子，文具文件夹薄板. 热成型片材. 汽车工业、玩具和花园家具的零件
| PROPERTY | Value | Unit | Method |
| Melt Flow Rate (230 oC, 2.16kg) | 6 | g/10min | ASTM D1238 |
| Density | 0.9 | g/cm3 | ASTM D1505 |
| Flexural Modulus | 1400 | MPa | ASTM D790 |
| Tensile Strength at Yield | 26 | MPa | ASTM D638 |
| Tensile Elongation at Yield | 9 | % | ASTM D638 |
| Izod Impact Strength (notched) at 23 oC | 170 | J/m | ASTM D256 |
| Vicat softening point (10N) | 152 | oC | ASTM D1525 |
| H.D.T. (0.46 Mpa) | 95 | oC | ASTM D648 |
用途
- 包装、汽车和消费品行业、行李、油漆桶、水桶、容器、板条箱、电池和大型玩具。
| PROPERTY | Value | Unit | Method |
| Melt Flow Rate (230 oC, 2.16kg) | 25 | g/10min | ASTM D1238 |
| Rockwell Hardness | 100 | R.Scale | ASTM D785 |
| Flexural Modulus | 1500 | MPa | ASTM D790 |
| Tensile Strength at Yield | 32 | MPa | ASTM D638 |
| Tensile Elongation at Yield | 13 | % | ASTM D638 |
| Izod Impact Strength (notched) at 23 oC | 30 | J/m | ASTM D256 |
| Vicat softening point (10N) | 152 | oC | ASTM D1525 |
| H.D.T. (0.46 Mpa) | 94 | oC | ASTM D648 |
用途
- 高熔体流动均聚物聚丙烯，用于以中高速纺丝生产 CF、BCF 和短纤维。适用于无纺布、尿布、医疗卫生应用和湿巾的低旦短纤维。